Abstract The industries that have polymers as an important raw material in their production, such as the construction, automotive, electrical and electronic sectors, always seek innovations to cut costs, reduce weight, easiness of processing, maximizing mechanical properties, and recyclability. In this context, this work presents the study of the kinetic parameters and viscoelastic behavior of a new thermoplastic system initially liquid. Through differential scanning calorimetry (DSC) analysis, Brookfield viscosimetry; dynamic-mechanical analysis (DMA) and mathematical modeling with consolidated and standardized methods, it was possible to evaluate the polymerization kinetics and viscoelastic behavior of the material in solutions with different concentrations. The generated equations allow the prediction of the kinetic and gelation behavior of the material reducing the need for laboratory tests to determine polymer properties. The found results showed that concentrations of benzoyl peroxide initiator with 1wt% in the methyl methacrylate (MMA) copolymer solution have the best viscoelastic and dynamic-mechanical properties with a less expensive polymerization cycle. production construction automotive sectors costs weight processing recyclability context liquid DSC (DSC viscosimetry dynamicmechanical dynamic DMA (DMA methods 1wt wt MMA (MMA cycle

ABSTRACT The addition of expanded graphite (EG) on environmentally friendly polymer matrix was systematically studied to produce carbon-polymer porous composite. Firstly, an appropriate EG was produced by monitoring the time and temperature of intercalated graphite thermal expansion while poly(furfuryl alcohol) (PFA) resin was obtained from the furfuryl alcohol polymerization. After PFA synthesis, different EG amounts of 0.2, 0.5, and 1.0 wt% were added in the resin and evaluated by viscosimetry and differential scanning calorimetry that showed EG helped in the crosslink formations decreasing the onset and endset temperatures. PFA resin kept a good fluidity, even for 1.0 wt% EG ensuring its homogeneous impregnation on the polyurethane foams. FTIR analyses confirmed the presence of functional groups on EG, which would contribute to the resin impregnation on the foam porous structure without changing the thermal resistance of the final product.